Analysis of the causes of concrete slump loss

If you are looking for high-quality products, please feel free to contact us and send an inquiry, email: brad@ihpa.net



Recently, the EU proclaimed new sanctions on Russia, including coal, timber, rubber, cement, and fertilizer, as well as high-end seafood concrete slump.

There are many reasons for slump loss, mainly in the following aspects:

1. Influence of raw materials

Whether the cement used and the pumping agent are matched and adapted must be obtained through the adaptability test. The optimum amount of the pumping agent should be determined through the adaptability test with the cement cementitious material. The amount of air-entraining and retarding components in the pumping agent has a greater impact on the loss of concrete slump. If there are many air-entraining and retarding components, the slump loss of concrete will be slow, otherwise the loss will be fast. The slump loss of concrete prepared with naphthalene-based superplasticizer is fast, and the loss is slow when the low positive temperature is below +5 °C.

If anhydrite is used as the setting modifier in the cement, the slump loss of the concrete will be accelerated, and the early strength component C3A content in the cement is high. If "R" type cement is used, the cement fineness is very fine, and the cement setting time is fast, etc. It will cause the slump loss of concrete to accelerate, and the speed of concrete slump loss is related to the quality and amount of mixed materials in the cement. The C3A content in the cement should be within 4% to 6%. When the content is lower than 4%, the air-entraining and retarder components should be reduced, otherwise the concrete will not solidify for a long time. When the C3A content is higher than 7%, it should be increased. Air-entraining retarder component, otherwise it will cause rapid loss of concrete slump or false setting phenomenon.

The mud content and mud block content of the coarse and fine aggregates used in concrete exceed the standard, and the content of crushed stone needle flake particles exceeds the standard, which will cause the slump loss of concrete to accelerate. If the coarse aggregate has a high water absorption rate, especially the crushed stone used, after being exposed to high temperature in the summer high temperature season, once it is put into the mixer, it will absorb a large amount of water in a short period of time, resulting in accelerated slump loss of the concrete in a short time (30min). 


2 Influence of stirring process

The concrete mixing process also affects the slump loss of concrete. The model of the mixer and the mixing efficiency are related. Therefore, the mixer is required to be regularly repaired and the mixing blades should be replaced regularly. Concrete mixing time should not be less than 30s. If it is less than 30s, the slump of concrete is unstable, resulting in relatively accelerated slump loss.


3 Temperature effects

The effect of temperature on the slump loss of concrete is of particular concern. In hot summer, when the temperature is higher than 25°C or above 30°C, the concrete slump loss will be accelerated by more than 50% compared with that at 20°C. When the temperature is lower than +5°C, the concrete slump loss will be very small or not lost. . Therefore, during the production and construction of pumped concrete, pay close attention to the influence of air temperature on the slump of concrete.

The high use temperature of the raw materials will cause the concrete to increase in temperature and accelerate the slump loss. It is generally required that the concrete discharge temperature should be within 5 ~ 35 ℃, beyond this temperature range, it is necessary to take corresponding technical measures, such as adding cold water, ice water, groundwater to cool down and heat the water and the use temperature of raw materials and so on.

It is generally required that the maximum operating temperature of cement and admixtures should not be higher than 50 °C, and the operating temperature of concrete pumped heating water in winter should not be higher than 40 °C. There is a false coagulation state in the mixer, and it is difficult to get out of the machine or transport it to the site for unloading.

The higher the temperature of the cementitious materials used, the worse the water-reducing effect of the water-reducing components in the pumping agent on concrete plasticization, and the faster the concrete slump loss. The concrete temperature is proportional to the slump loss, and the slump loss can reach about 20-30mm when the concrete increases by 5-10℃.


4 Strength levels

The slump loss of concrete is related to the strength grade of concrete. The slump loss of concrete with high grade is faster than that of low-grade concrete, and the loss of crushed stone concrete is faster than that of pebble concrete. The main reason is that it is related to the amount of cement per unit.


5 Concrete state

Concrete statically loses slump faster than dynamic. In the dynamic state, the concrete is continuously stirred, so that the water-reducing components in the pumping agent cannot fully react with the cement, which hinders the progress of cement hydration, so that the slump loss is small; in the static state, the water-reducing components are fully in contact with the cement, The cement hydration process is accelerated, so the concrete slump loss is accelerated.


6 Transport machinery

The longer the transportation distance and time of the concrete mixer truck, the less free water of the concrete clinker due to chemical reaction, water evaporation, water absorption of the aggregate and other reasons, resulting in the loss of concrete slump over time. The barrel also causes mortar loss, which is also an important cause of concrete slump loss.


7 Pour speed and time

In the process of concrete pouring, the longer the time for the concrete clinker to reach the silo surface, the rapid reduction of free water in the concrete clinker due to chemical reactions, water evaporation, aggregate water absorption and other reasons, resulting in slump loss. , especially when the concrete is exposed on the belt conveyor, the contact area between the surface and the external environment is large, and the water evaporates rapidly, which has the greatest impact on the slump loss of the concrete. According to the actual measurement, when the air temperature is around 25℃, the on-site slump loss of concrete clinker can reach 4cm within half an hour.

Concrete pouring time is different, which is also an important cause of concrete slump loss. The impact is small in the morning and evening, and the impact is greater at noon and afternoon. The temperature in the morning and evening is low, the water evaporation is slow, and the temperature in the afternoon and afternoon is high. The worse the fluidity and cohesion, the more difficult it is to guarantee the quality.


TRUNNANO is a concrete additives supplier with over 12 years experience in nano-building energy conservation and nanotechnology development. We accept payment via Credit Card, T/T, West Union and Paypal. Trunnano will ship the goods to customers overseas through FedEx, DHL, by air, or by sea.

If you are looking for high quality concrete superplasticizer, please feel free to contact us and send an inquiry.

sales@cabr-concrete.com




According to the bank of Spain's latest forecast data, the average inflation is expected to hit 7.6% in 2022, but the average wage increase for workers in this country is expected to be less than 4% in 2022. 

If the Bank of Spain's forecast comes true, the gap between price and wage growth in Spain in a single year will be the largest since 1984.

Prices in Spain rose 9.8% year on year in March 2022 and average wages rose 2.4% year on year, with the Bank of Spain forecasting that the country's inflation rate will improve from July.

Recent changes in the international situation have had a big impact on commodity and energy prices. How the prices of the concrete slump will develop in the future is still uncertain.

Inquiry us

High Purity Iron powder Fe Powder CAS 7439-89-6, 99%

High Purity Tungsten Carbide WC Powder Cas 12070-12-1, 99%

High Purity Spherical Graphite C Powder CAS 7782-42-5, 99.9%

High Purity Copper Oxide CuO powder CAS 1317-38-0, 99.9%

High Purity Colloidal Gold Nano Gold Solution CAS 7440-57-5

How to determine the optimum dosage of concrete superplasticizer

Factors affecting the effect of concrete superplasticizer

Why should polycarboxylate superplasticizer be added to concrete

What Role Do Early Strength Agents Play?

What is the 3D Printing Metal Powder

What are Ni-Ti Alloys?

What are Commonly Used Milling Cutter Coatings?

What Is Graphite Lubricant?

The rising price of coke also has a certain impact on the price of the automatic cut to length line

How does Concrete Superplasticizer Change the Strength of Concrete?

Researchers Developed Graphene-based Foam Composites For Efficient Water Filtration

What is Manganese Dioxide MnO2 Used For?

What is Boron Carbide Used For?

What are Molecular Sieves Used For?

What is Nano Silica Used For?

Our Latest Answers

What is a polycarboxylate superplasticizer

In 2023, the China Greater Bay Area Concrete Industry High-Quality Development Seminar and the Expo on Concrete Equipment and Technology will take place at the Guangzhou Canton Fair Complex. Guangzhou Canton Fair Complex. The conference's theme will…

What is Molybdenum disulfide MoS2 powder

Description of Molybdenum diulfide Molybdenum disulfide (also known as MoS2) is a transition metal sulfide. It is dark grey, or black, solid. The layers of the crystal structure are made of alternately arranged molybdenum-sulfur atoms. Molybdenum d…

Why does properly poured concrete end up cracking

It is very easy to cause concrete cracking if the construction or maintenance are not done correctly. What are then the five main causes of cracking concrete? 1. The cement proportion problem: Some workers in construction will add more water for a mo…